copper anti-seize 3

[[email protected]]

the BB un-fixed cup turned out so i pulled the alum crank from the
steel 3S spindle. the copper went on four weeks ago and a 4 week
monsoon ensued giving the copper a test. crank pulled easy, spindle
shows no rust, and remaining rust pits on the 3S taper were black but
mostly empty holes. i did run linseed onto the inner crank/spindle
surfaces after the locktite setup in 3-4 days.
that's superior short term result to the aluminum anti-seize in the
rust/pull areas

 

[[email protected]]

heat tube before using-hot sun ect> copper ingreedyant disperese thru
carrier more evenly when hot
possible also that a hot virgin tube will not cause fluid seperation
problems

 

[[email protected]]

heat tube before using-hot sun ect> copper ingreedyant disperese thru
carrier more evenly when hot
possible also that a hot virgin tube will not cause fluid seperation
problems

 

[[email protected]]

heat tube before using-hot sun ect> copper ingreedyant disperese thru
carrier more evenly when hot
possible also that a hot virgin tube will not cause fluid seperation
problems

 

[[email protected]]

heat tube before using-hot sun ect> copper ingreedyant disperese thru
carrier more evenly when hot
possible also that a hot virgin tube will not cause fluid seperation
problems